5a05 is an aluminum alloy from the Al Mg series that is resistant to rust. Unlike other alloys, it cannot be strengthened through heat treatment. It has a higher magnesium content and lower strength, similar to the 5A03 alloy. The strength of the alloy can be increased by cold deformation, but this also reduces its plasticity. In its annealed state, the alloy has relatively high plasticity, while in the semi cold worked hardened state, the plasticity is still acceptable. It has good resistance to corrosion and can be easily welded using spot welding, atomic hydrogen welding, gas welding, and argon arc welding. However, its machinability and annealing state are not very good, while the semi cold work hardening state is still acceptable.
| Product | Contract No. | Lot No. | ||||||||||
| Dimension (mm) | 1.2-200 | Alloy | 5A05 | Piece Count | ||||||||
| Techuique Standard | GB/T3190--1996/EN | Weight(kg) | ||||||||||
| Chemical Composition(%) | ||||||||||||
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Others | Al | ||
| Standard | 0.5 | 0.5~1.0 | 0.1 | 0.3-0.6 | 4.8-5.5 | - | - | 0.2 | 0.15 | 0.15 | Remain | |
| Notice:Aluminum foil not contains Pb、As and other Virose elements | ||||||||||||
| Mechanical Property | ||||||||||||
| Temper | Thickness | Tensile Strength（Mpa） | Strength(Mpa) | Elongation% | Cup Bulge | |||||||
| O | 1.2-6.3 | 290-365 | 130-205 | - | - | |||||||
| 6.31-80 | 285-360 | 125-205 | 14 | - | ||||||||
| 80.1-120 | 275 | 120 | 12 | - | ||||||||
| 120.1-160 | 270 | 115 | 12 | - | ||||||||
| 160.1-200 | 265 | 105 | 10 | - | ||||||||
| H112 | 6.3-40 | 290 | 130 | 10 | - | |||||||
| 40.1-80.0 | 285 | 125 | 10 | - | ||||||||
| H116 | 1.6-30 | 315 | 230 | 10 | - | |||||||
| 30.1-40 | 305 | 215 | 10 | - | ||||||||
| 40.1-80.0 | 285 | 200 | 10 | - | ||||||||
| 80.1-110 | 275 | 170 | 10 | - | ||||||||
| H321 | 4.0-12.5 | 315-405 | 230-315 | - | - | |||||||
| 12.51-40.0 | 305-385 | 215-305 | 10 | - | ||||||||
| 40.1-80.0 | 385-385 | 200-295 | 10 | - | ||||||||
| H323 | 1.2-6.3 | 330-400 | 250-315 | - | - | |||||||
| H343 | 1.2-6.3 | 365-435 | 285-350 | - | - | |||||||
Productivity: 1200 tons per month Transportation: Ocean,Land
Place of Origin: China Supply Ability: 1050 tons per month
Certificate: ISO9001 HS Code: 76061199
Payment Type: L/C,T/T In co term: FOB,CFR,CIF,EXW
Commonly used in manufacturing welded pipelines, welded oil tanks, and other liquid containers that require high process shaping, good corrosion resistance, and medium load capacity, as well as other parts; Wire used as welding rods and rivets requires anodizing treatment. It is also used for making armor plates, high-strength structural components, storage tanks, pressure vessels, and marine product components